Effect of Conditioning Protocols and Ultrasonic Application of an Infiltrant Resin in White Spot Lesions.

The aim of this study was to evaluate different conditioning protocols and sonic/ultrasonic application of an infiltrant resin (IR) in artificial white spot lesions (AWSL). the V/L surfaces of 48 molars were induced to an AWSL and divided in 6 groups, according to the conditioning protocols and application technique: 15% hydrochloric acid (HA) + manual application of the IR; HA + 37% phosphoric acid (PA) + manual application of the IR; HA + ultrasonic application (U) of the IR; HA + sonic application (S) of the IR; PA+HA+S; and PA+HA+U. For the Penetration Depth (PD), the crowns were etched with HA for 120s. The IR Icon® (DMG) was applied according to the manufacturer`s instructions. The crowns were dye penetrated (0.1% red fluorophore rhodamine B isothiocyanate for 12h) and bleached with 30% hydrogen peroxide for 12 h. The discs were immersed in a 50% ethanol solution, containing 100 µM of sodium fluorescein. The PD (in µm) was measured using confocal laser scanning microscopy (20x). The bond strength (BS) was performed by michoshear test (0.5 mm/min). Data were submitted to 2-way ANOVA and Tukey (α=0.05). For BS, the interaction was not significant (p>0.05). For PD, the main factors were significant (application - p<0.001; conditioning technique - p=0.003). The ultrasonic application showed the highest PD values. PA+HA presented higher results than HA. The sonic/ultrasonic applications and the use of phosphoric acid prior to hydrochloric acid improved PD of the infiltrant resin. Conditioning protocols or application techniques did not influence BS values.

Effect of conditioning protocols and ultrasonic application of an infiltrant resin in white spot lesions

Abstract The aim of this study was to evaluate different conditioning protocols and sonic/ultrasonic application of an infiltrant resin (IR) in artificial white spot lesions (AWSL). the V/L surfaces of 48 molars were induced to an AWSL and divided in 6 groups, according to the conditioning protocols and application technique: 15% hydrochloric acid (HA) + manual application of the IR; HA + 37% phosphoric acid (PA) + manual application of the IR; HA + ultrasonic application (U) of the IR; HA + sonic application (S) of the IR; PA+HA+S; and PA+HA+U. For the Penetration Depth (PD), the crowns were etched with HA for 120s. The IR Icon® (DMG) was applied according to the manufacturer`s instructions. The crowns were dye penetrated (0.1% red fluorophore rhodamine B isothiocyanate for 12h) and bleached with 30% hydrogen peroxide for 12 h. The discs were immersed in a 50% ethanol solution, containing 100 µM of sodium fluorescein. The PD (in µm) was measured using confocal laser scanning microscopy (20x). The bond strength (BS) was performed by michoshear test (0.5 mm/min). Data were submitted to 2-way ANOVA and Tukey (α=0.05). For BS, the interaction was not significant (p>0.05). For PD, the main factors were significant (application - p<0.001; conditioning technique - p=0.003). The ultrasonic application showed the highest PD values. PA+HA presented higher results than HA. The sonic/ultrasonic applications and the use of phosphoric acid prior to hydrochloric acid improved PD of the infiltrant resin. Conditioning protocols or application techniques did not influence BS values.

Resumo: O objetivo deste estudo foi avaliar diferentes protocolos de condicionamento e a aplicação sônica/ultrassônica de uma resina infiltrante (RI) em lesões de mancha branca produzidas artificialmente (LMBA). As superfícies vestibulares/linguais de 48 molares foram induzidas à formação de LMBA e divididas em 6 grupos, de acordo com os protocolos de condicionamento e técnica de aplicação da resina infiltrante: ácido hidroclorídrico 15% (AH) + aplicação manual da RI; AH + ácido fosfórico 37% (AF) + aplicação manual da RI; AH + aplicação ultrassônica da RI (U); AH + aplicação sônica da RI (S); AF + AH + S; e AF + AH + U. para o grau de penetração (GP), condicionou-se as coroas com AH por 120 s. A RI Icon® (DMG) foi aplicada de acordo com as instruções do fabricante. As coroas foram coradas (rodamina B 0,1% por 12 h) e clareadas com peróxido de hidrogênio 30% por 12 h. os discos foram imersos em solução de etanol 50%, contendo 100 µM de fluoresceína sódica. O GP (em µm) foi mensurado por meio de microscopia confocal a laser (20´). A resistência de união (RU) foi calculada pelo teste de microcisalhamento (0,5 mm/min). Os dados foram submetidos ao teste ANOVA 2 fatores e Tukey (α=0,05). Para RU, a interação não foi significante (p>0,05). Para GP, os fatores principais foram significantes (técnica de aplicação - p<0,001; protocolos de condicionamento - p=0,003). A aplicação U mostrou os maiores valores de GP. AF+AH demonstrou resultados superiores ao grupo AH. As aplicações sônica/ultrassônica e o uso do ácido fosfórico antes do ácido hidroclorídrico aumentaram o GP da resina infiltrante. Os protocolos de condicionamento ou as técnicas de aplicação não influenciaram os valores de RU.